TLS-301 Modified Epoxy Barrel Rubber Glue

TLS-301 is manufactured with advanced formulation, modified epoxy resin, excellent modified alicyclic curing agent, and reasonable equipment and process. It has excellent comprehensive performance and is used in drier environment without wet stains. In the solid substrate such as concrete, anchoring steel bars, anchors, bolts, etc., such as the post-buried ribs of the frame structure wall, structural reinforcement and transformation, equipment fixed installation, indoor and outdoor decoration projects.

400 660 2636

TLX@njtelesun.com

Category

Structural adhesive

Product Inquiry Related products

Product Details

▲ Solidified at room temperature, high strength, strong adhesion and good durability.

▲ According to different use environments, different use requirements to design different formulations.

▲ Anti- aging and acid and alkali resistance, excellent resistance to water and other media.

▲ Component A and Component B have a wide distribution of glue, which is convenient for on- site operation.

▲ As expected, the rear reinforcement has superior load-displacement characteristics.

▲ Good temperature resistance, which can be welded after burying, the glue is environmentally friendly, safe and non- toxic.

Main Performance Parameters

Performance item Performance ltem			lndex parameters lndex parameter	Check condition
Colloidal performance Glue performance	Splitting tensile strength (MPa)		≥ 8.5	Curing 7d, tested at 2mm/min loading speed at (23±2) ° C, (50±5)% RH loading speed at (23±2) ° C, (50±5)% RH
	Bending strength (MPa)		≥ 50
	Compressive strength (MPa)		≥ 60
Bonding capability	Steel-steel tensile shear strength standard value (MPa)		≥ 16	Curing 7days, tested under (23±2)℃, (50±5)%RH
	Ribbed steel bars under constrained drawing conditions (MPa)	C30 Φ25(HRB335) L=150 mm	≥ 11.0
		C60 Φ25(HRB335) L=125 mm	≥ 17.0
Nnvolatile content (solid content)%		≥ 99		(105±2)℃,(180±5)min

The Chemical Response Time is Shown in the Following Table

Component dispensing glue ratio: A:B=3:1

Operable time and curing time (see table below)

Temperature of base materials	Operable Time (min)	Curing time (h)
5	≥ 60	90
15	≥ 45	72
25	≥ 30	48
35	≥ 20	24

The curing time refers to the time required for the colloid to reach 85% of the standard value of the strength. After the curing time is reached, the next step can be carried out.

Construction Steps

Package Specifications

Name	Specification	Component	Transportation	Storage
TLS-301 Modified epoxy cartridge-type rebar anchoring adhesive	10 kg	A: 7.5 kg	This product is non-toxic and non-hazardous. According to general chemical building material transportation standards.	Product stored under low-temperature drying conditions (25°C) Shelf life: one year
		B: 2.5 kg